@thesis{thesis,
		author={Prihatno  Asep},
		title ={Analisa Pengaruh Letak Susunan Serat Ampas Tebu (Baggase) Terhadap Kekuatan Tarik Menggunakan Epoxy},
		year={2020},
		url={http://eprints.polbeng.ac.id/289/},
		abstract={Bagasse fiber (baggase) is an organic waste that is widely available in various regions in Indonesia. This research was conducted to determine the strenght of sugarcane bagasse as a substitute composite in which this study conducted variations in the variation of the composition of the fiber woven, cross, and random by comparison volume ratio of epoxy 92 %, 88 %, 84 % with natural fibers 8 %, 12 %, 16 % by performing tensile test testing with ASTMD 638-14 standard by using the hand lay up method composite printing. The results of the tensile test of bagasse fiber for 8% weight of the highest were cross and random fibers of 15.16 MPa, for 12% of weight the highest were cross and random fibers which had a value of 18.71 Mpa, for 16% fibers which had The highest tensile strength values were woven and cross fibers which had a value of 21.69 MPa. This study shows that the addition of sugar cane fiber affects the tensile strength.}
		}