		title ={ANALISIS KEKUATAN BENDING PADA KOMPOSIT
SERAT KARBON DAN KOMPOSIT SERAT ARAMID
MENGGUNAKAN RESIN EPOXY},
		year={2023},
		url={http://eprints.stta.ac.id/1022/},
		abstract={The aviation industry is very fast where in this industry requires components 
to build an airplane from various kinds of metal and non-metal materials. This study 
focuses on bending testing to determine the bending strength between Carbon fiber 
and Aramid fiber. The manufacture of Carbon fiber and Aramid Woven Roving fiber 
composites [0 °, 90°] uses the hand lay up method, referring to the ASTM (American 
Society for Testing Material) D790-02 standard. And use Epoxy resin. Results of the 
bending test for carbon fiber and aramid fiber were obtained at 60% volume 
fraction, the bending strength value was higher than the 70% volume fraction for 
both fiber types, namely 17.558 MPa for carbon fiber and 17.338 MPa for Aramid 
fiber. macro photo testing of carbon fiber and aramid fiber observed that aramid 
fiber is more ductile than carbon fiber.}
		}