		title ={STUDI EKSPERIMEN KEKUATAN BENDING KOMPOSIT SERBUK TONGKOL JAGUNG DAN SERBUK KAYU JATI BERMATRIKS RESIN EPOKSI SEBAGAI BAHAN KANDIDAT SAYAP PESAWAT TANPA AWAK},
		year={2023},
		url={http://eprints.stta.ac.id/1142/},
		abstract={The development of technology in the manufacturing industry, especially 
in the production of unmanned aerial vehicles, has resulted in significant 
progress. Composites are formed from a combination of two or more materials 
with different mechanical properties. The matrix acts as a binding material, while 
the reinforcement acts as a strengthening material. Powder is generally used as 
reinforcement in composites.
This study aims to test the bending strength of teak sawdust composites 
with a volume fraction of 10% corncob powder - 20% teak wood powder - 70% 
epoxy resin and hardener, 10% corn cob powder - 30% teak wood powder - 60% 
resin epoxy and hardener, 10% corncob powder ? 40% teak sawdust - 50% epoxy 
resin and hardener. The standard used in the test is ASTM D 790-99 for bending 
strength.
The results showed that the highest bending strength in the volume 
fraction of 10% corn cob powder and 20% teak wood powder was 34.414 N/mm2
while the lowest bending strength in the volume fraction of 10% corn cob powder 
and 40% teak wood powder was 16.133 N/mm2. The higher the volume fraction of 
teak sawdust, the bending strength of the composite will tend to decrease.}
		}