@thesis{thesis,
		author={PRATAMA ANGGARA SAPUTRA  BAYJURI},
		title ={PENGARUH VARIASI ARUS DAN WAKTU 
ELEKTROPLATING KUNINGAN TERHADAP KEKERASAN 
PADA BAJA KARBON RENDAH},
		year={2020},
		url={http://eprints.stta.ac.id/1911/},
		abstract={Steel is one kind of low carbon steel. In general, low-carbon steel is ductile, 
tough, relatively cheap, and has good weldability and machinibilty. However, 
one of the weaknesses of low carbon steel is the low hardness values. One ef ort 
to improve the resistance of the steel is electroplating.
In this research, electroplating process used the current variations of 2A,
4A and 6A and the time variations of 10 minutes, 20 minutes and 30 minutes. 
The hardness testing used vickers method. The test results showed that the 
coating formed on the electroplating process wasstrongly effected by the time 
and flow coating process. The results of hardness testing on the surface after 
electroplating, the highest value was 0,042 VHN at 4A current and 30 minutes.}
		}