@thesis{thesis,
		author={JORDY  ALESANDRO},
		title ={ANALISIS KEKUATAN SAMBUNGAN FRICTION STIR WELDING 
MENGGUNAKAN TOOL STAINLESS STEEL DENGAN VARIASI SUDUT 
KEMIRINGAN SPINDLE 0°, 3° DAN 6° PADA MATERIAL AL 2024-T3},
		year={2020},
		url={http://eprints.stta.ac.id/1944/},
		abstract={Friction stir welding is a welding process that utilizes heat by friction 
between the tool and the base metal, and the plastic deformation of the base metal 
is caused by stirring the tool. The selection of material tools and determining the 
tilt tools are important parameters in the friction stir welding process. This research 
was conducted to determine the results of the friction stir welding joint strength, 
where the welding joint results will be carried out a macro structure photo process 
to know the friction stir welding zone.
The method of joining the material is carried out by the friction stir welding 
process using stainless steel tools and the tools tilt angle is 0°, 3° and 6°, with plate?shaped specimens. After the friction stir welding process is carried out, the next 
step is making a tensile test specimen based on ASTM E8/E8M-09. Then tensile 
testing is performed to know the strength results of the welding joint and taking 
photograph of macro structure to know the friction stir welding zone.
In this research the highest friction stir welding joint strength results with a 
6° tilt angle variation, with an average value of ultimate tensile strength of 238,665 
MPa. While the average value of ultimate tensile strength with a tilt angle variation 
of 3° is 199,311 MPa. While the value ultimate tensile strength with a tilt angle 
variation of 0° only has one specimen is 30,305 MPa. The resulting zones in the 
friction stir welding process are unaffected zone, thermomechanically affected zone 
and weld nugget.}
		}