		title ={Penelitian Beton Dengan Penambahan Abu Sekam Padi Dan Limbah Keramik Sebagai Substitusi Semen},
		year={2020},
		url={http://repository.unik-kediri.ac.id/225/},
		abstract={Concrete is a technology that continues to develop in the construction sector. The need for concrete-forming materials continues to increase in terms of costs, so there is a need for innovation in the use of concrete mixtures. One of them is using the innovation of rice husk ash and ceramic waste, both of these materials are contained in the cement content, namely rice husk ash containing silica and ceramic waste containing alumina. The method used refers to the Indonesian National Standard with a cylindrical specimen measuring 15x30 cm tested at the age of 28 days and the planned quality is fc '14.5 Mpa. The research objective was to determine the compressive strength and slump value by adding a mixture of rice husk ash 3%, 6%, 9%, 12% and ceramic waste 3% by weight of cement. The results showed that the slump value decreased with the lowest value of 13.5 cm. the results of the compressive strength of concrete with the addition of rice husk ash and ceramic waste have not been able to achieve the planned quality. The highest average compressive strength value was found in the addition of rice husk ash 9% with ceramic waste 3%, namely 6.53 Mpa.

Keywords : Lightweight Concrete, Rice Husk Ash, Ceramic Waste}
		}